Standard：
JIS H4600 TR270C0.2pd，ASTM B265 Gr.11
Chemical Compositions:
% | Ti | Pd | N | C | H | Fe | O |
MIN. | Surplus | 0.12 | |||||
MAX. | 0.25 | 0.03 | 0.08 | 0.013 | 0.250 | 0.15 |
Physical Properties:
Density | 4.51 g/cm3 |
Grain Size | 3.0-7.0 |
Mechanical Properties:
Tensile Strength: 270Mpa≥σb≤410Mpa
Yield Strength σb ≥ 165Mpa
Elongation: δ ≥ 27%
Corrosion Resistance：
Titanium has strong corrosion resistance in more media, especially in neutral and oxidizing media is very strong corrosion resistance, can also be used in some dilute reducing acids, such as room temperature until the boiling point of various concentrations of nitric acid. Good corrosion resistance to most alkali solutions, such as room temperature barium hydroxide, calcium hydroxide, magnesium hydroxide saturated solution, but not for boiling sodium hydroxide solution. Titanium is completely non-corrosive in seawater, and very resistant to corrosion in most organic acids (except formic acid and oxalic acid). Excellent corrosion resistance in wet chlorine gas and chloride solutions such as chlorite and hypochlorite. Corrosion resistance in sodium chloride solution increases with the increase of solution pH
Application：
Aerospace, plate heat exchanger, bellows compensator expansion joint, seawater desalination, desulfurization and denitrification, chemical equipment, etc.
Matching Welding Consumables：
ERTi-11
Supply Style：
Plate, strip, bar, wire, forgings, light bar, welding consumables, flanges, etc., as per the drawing
Origin of Product：
Kobe, Japan/ATI, USA
Standard：
JIS H4600 TR270C0.2pd，ASTM B265 Gr.11
Chemical Compositions:
% | Ti | Pd | N | C | H | Fe | O |
MIN. | Surplus | 0.12 | |||||
MAX. | 0.25 | 0.03 | 0.08 | 0.013 | 0.250 | 0.15 |
Physical Properties:
Density | 4.51 g/cm3 |
Grain Size | 3.0-7.0 |
Mechanical Properties:
Tensile Strength: 270Mpa≥σb≤410Mpa
Yield Strength σb ≥ 165Mpa
Elongation: δ ≥ 27%
Corrosion Resistance：
Titanium has strong corrosion resistance in more media, especially in neutral and oxidizing media is very strong corrosion resistance, can also be used in some dilute reducing acids, such as room temperature until the boiling point of various concentrations of nitric acid. Good corrosion resistance to most alkali solutions, such as room temperature barium hydroxide, calcium hydroxide, magnesium hydroxide saturated solution, but not for boiling sodium hydroxide solution. Titanium is completely non-corrosive in seawater, and very resistant to corrosion in most organic acids (except formic acid and oxalic acid). Excellent corrosion resistance in wet chlorine gas and chloride solutions such as chlorite and hypochlorite. Corrosion resistance in sodium chloride solution increases with the increase of solution pH
Application：
Aerospace, plate heat exchanger, bellows compensator expansion joint, seawater desalination, desulfurization and denitrification, chemical equipment, etc.
Matching Welding Consumables：
ERTi-11