English 
Origin of Product：
Otokumpu, Sweden/Nisshin Steel
Standard：
ASTM A240/ASME SA-240、ASTM A276、ASTM A182/ASME SA-182、ASTM A312/ASMES A312
Main Chemical Compositions：
C:≤0.08
Mn:≤2.0
Ni:19.0～20.0
Si:≤1.5
Cr:24.0～26.0
Mo:≤0.030
P:0.≤0.045
Physical Properties：
Density of 310S：7.98g/cm3
Mechanical Properties：
Tensile Strength：σb≥515Mpa
Yield Strength：σb≥205Mpa
Elongation：δ≥35%
Hardness: ≤310（HB）
Corrosion Resistance：
310S stainless steel has good high temperature resistance, the temperature exceeds 800 [1], it begins to soften, the allowable stress begins to continue to reduce, the maximum use temperature of 1200 ℃. Because of the high content of nickel (Ni) and chromium (Cr), it has good resistance to oxidation, corrosion, acid and alkali, high temperature resistance, high temperature resistant steel pipe is used for manufacturing electric heating furnace tubes and other occasions, austenitic stainless steel with increased carbon content, due to its solid solution strengthening effect to improve the strength, austenitic stainless steel chemical composition characteristics of chromium and nickel based on the addition of elements such as molybdenum, tungsten, niobium and titanium, due to its organization of The chemical composition of austenitic stainless steel is characterized by the addition of chromium and nickel based on elements such as molybdenum, tungsten, niobium and titanium.
Application：
Petroleum, electronics, chemical, pharmaceutical, light textile, food, machinery, construction, nuclear power, aerospace, military industry and other industries
Matching Welding Consumables：
ER310
Supply Style：
Sheets/Plates
Origin of Product：
Otokumpu, Sweden/Nisshin Steel
Standard：
ASTM A240/ASME SA-240、ASTM A276、ASTM A182/ASME SA-182、ASTM A312/ASMES A312
Main Chemical Compositions：
C:≤0.08
Mn:≤2.0
Ni:19.0～20.0
Si:≤1.5
Cr:24.0～26.0
Mo:≤0.030
P:0.≤0.045
Physical Properties：
Density of 310S：7.98g/cm3
Mechanical Properties：
Tensile Strength：σb≥515Mpa
Yield Strength：σb≥205Mpa
Elongation：δ≥35%
Hardness: ≤310（HB）
Corrosion Resistance：
310S stainless steel has good high temperature resistance, the temperature exceeds 800 [1], it begins to soften, the allowable stress begins to continue to reduce, the maximum use temperature of 1200 ℃. Because of the high content of nickel (Ni) and chromium (Cr), it has good resistance to oxidation, corrosion, acid and alkali, high temperature resistance, high temperature resistant steel pipe is used for manufacturing electric heating furnace tubes and other occasions, austenitic stainless steel with increased carbon content, due to its solid solution strengthening effect to improve the strength, austenitic stainless steel chemical composition characteristics of chromium and nickel based on the addition of elements such as molybdenum, tungsten, niobium and titanium, due to its organization of The chemical composition of austenitic stainless steel is characterized by the addition of chromium and nickel based on elements such as molybdenum, tungsten, niobium and titanium.
Application：
Petroleum, electronics, chemical, pharmaceutical, light textile, food, machinery, construction, nuclear power, aerospace, military industry and other industries
Matching Welding Consumables：
ER310
Supply Style：
Sheets/Plates